Ọkpụrụkpụ nkịtị | Anya nke ọ bụla isi n'elu elu nke veneer na deviates si ìhè arọ ogologo achị | |
Ogologo veneer 500 | Ogologo veneer 1000 | |
≤15 | 2.0 | 4.0 |
15...≤25 | 1.5 | 3.0 |
25...≤60 | 1.0 | 2.0 |
> 60 | 1.0 | 1.5 |
Ogo ọdịdị
Ihe | Oke ekwenyere |
Ọzịza | Ekweghị |
Mgbawa | |
Knot nwụrụ anwụ | |
Adhering-ahụ nke mba ọzọ | |
oghere ahụhụ | |
ire ere | |
Mmetọ | |
Ọkụkụ | Enwere ike ole na ole, enweghị mmetụta na ojiji |
Mmetụta | |
Agba-ọdịiche na nfesa | |
Patches kwa sq.m n'elu | ≤3 |
Ihe Nnwale GB- Tupu nnyefe ụlọ ọrụ nyocha
Nwale Ihe | Nkeji | Ọkọlọtọ | Usoro ule | |
Ike na-ehulata kwụ ọtọ | Maka A | Mpa | ≥65 | GB/T2634—Ọkọlọgụ ule 2008 |
Maka B | ≥65 | |||
Module ịgbagọ kwụ ọtọ nke ngbanwe | Maka A | Gpa | ≥8 | |
Maka B | ≥8 | |||
Nkwekọrịta (n'okpuru 20MPa) | Maka C | % | ≤3 | |
Crev | ≥70 | |||
Ike mmetụta (nnwale akụkụ) | Maka A | KJ/㎡ | ≥13 | |
Maka B | ≥13 | |||
Interlaminar ike shiee | Mpa | ≥8 | ||
Ike eletrik kwụ ọtọ (90 ℃ + 2 ℃) | KV/mm | ≥11 | ||
Ike eletrik kwụ ọtọ (90 ℃ + 2 ℃) | KV | ≥50 | ||
Njupụta arụmọrụ | g/cm³ | > 1.1-1.2 | ||
mmiri ọdịnaya | % | ≤6 | ||
Mbelata mgbe ihicha | Maka A | % | ≤0.3 | |
Maka B | ≤0.3 | |||
N'ebe ọkpụrụkpụ | ≤3 | |||
Ntinye mmanụ | % | ≥8 |